Evaluation of wet tensile shear strength and surface properties of finger-jointed acetylated beech (Fagus sylvatica L.) laminated veneer lumber
Abstract
Abstract Experiments on finger-jointing acetylated beech ( Fagus sylvatica L.) laminated veneer lumber (LVL) have been made. The specimens were examined on its wet tensile shear strength (TSS) using three adhesives, including phenol resorcinol formaldehyde (PRF), one-component polyurethane (PUR) (without primer), and melamine urea formaldehyde (MUF). Contact angles (CA) of uncured and drop-applied MUF, PRF, and PUR adhesives on freshly cut finger-joints were evaluated. Surface roughness was measured using a laser-scanning-microscope (LSM). Results showed that PRF bonded acetylated specimens had highest wet TSS, followed by specimens with PUR bonding. MUF performed poorly, which was most likely caused by its inadequate water resistance and changes in chemical reactions due to remaining acetic acid. Acetylated finger-joints had a topography similar to untreated joints. Moreover, CA were just barely lower for MUF and PRF on acetylated wood than on untreated references.
Reference
Maik Slabohm; Hannes Stolze; Holger Militz. (2023). Evaluation of wet tensile shear strength and surface properties of finger-jointed acetylated beech (Fagus sylvatica L.) laminated veneer lumber. European Journal of Wood and Wood Products. https://doi.org/10.1007/s00107-023-01970-3
Explore the literature
Follow references, discover citing works and find related studies.